The TQC Impact Test is used to determine the impact resistivity and flexibility of coatings. The dual scale instrument is equipped with a special guidance which assures that the distance between each impact is always according to the standard. For correct positioning a spirit-level is built-in. Each Impact test comes as a complete set (instrument and accessoires) to perform a test according DIN/ISO 6272, ASTM D2794 and ASTM G14
Mandatory test in Qualicoat, QIB and GSB accredited laboratories.
Documents
Standards for impact testing
Below mentioned standards are a list of the possible standards. If the required standard is not listed below please contact TQC to check if adoption of this standard is possible*:
SP1880 | SP1890 | SP1891 | SP1895 | SP1896 | |
| Type of Impact | Indirect | Direct | Direct | Direct | Direct |
| ISO 6272-1:2002 |
| • |
|
|
|
| ISO 6272-2:2002 | • |
|
|
|
|
| ISO 6272:1993 |
|
| • |
|
|
| ASTM D 2794:2004 | • |
|
|
|
|
| ASTM G14-04 |
|
|
| • |
|
| JIS K 5600-5-3:1989 | • | • |
|
|
|
| EN 12206-1:2004 | • |
| • | • |
|
| EN 13523-5:2001 | • | • |
|
|
|
| AAMA 2605-05 | • |
| • |
|
|
| Qualicoat 2006 | • |
| • |
|
|
| Qualisteelcoat 2008 | • |
| • |
|
|
| Canadian Standards Association (CSA) |
|
|
|
| • |
* Conformation to a required standard depends on the impact tester type. The combination of items can change to comply with another standard.
ORDERING INFORMATION
SP1880
TQC Impact Test according to ISO 6272-2 and ASTM D2794
Type: Indirect Impact Tester
Content: Base plate assembly, guide tube, release collar, punch Ø12.7 mm , punch Ø15.9 mm, weight 1 kg, die Ø16.3 mm. Max test panel thickness: 4,5 mm
SP1890
TQC Impact Test according to ISO 6272-1
Type: Direct Impact Tester
Content: Base plate assembly, guide tube, release collar, clamp device, ball Ø20 mm, die 27mm, weight 1 kg. Max. test panel thickness: 1,25mm
SP1891
TQC Impact Test according to ISO 6272-1 and ASTM D2794 (before 1993)
Type: Direct Impact Tester
Content: Base plate assembly, guide tube, release collar, clamp device, ball Ø20 mm, die 27mm, weight 1 kg, ball Ø15.9 mm, die 16.3mm, weight 0.9 kg
SP1895
TQC Impact Test according to ASTM G14
Type: Direct Impact Tester
Content: Base plate assembly, guide tube, release collar, punch Ø15.9 mm, weight 1.361 kg and a V-notch vise with spring clamp to hold the pipe
SP1896
TQC Impact Test according to CSA
| Weight | 2 lbs |
|---|---|
| Dimensions | 51 × 3 × 3 in |
| Model | SP1880, SP1890, SP1891, SP1895, SP1896 |
Type: Indirect Impact Tester
Content: Base plate assembly, guide tube, release collar,
punch & Oslash: 12.7 mm , punch Ø
Related products
- ASTM D522, Elasticity Testing, ISO 6860, Resistance & Deformation
Bend Test Conical Mandrel Basic – SP1831
ASTM D522, Elasticity Testing, ISO 6860, Resistance & DeformationBend Test Conical Mandrel Basic – SP1831
The TQC Conical Bend Test “Basic” is a simplified version of the TQC Conical Bend Test “Pro” (SP1830) It is a laboratory apparatus to bend coated test panels over a conical shaped mandrel in order to assess the elasticity or resistance of a coating-, paint or varnish to cracking, elongation and/or detachment from a metal test panel in accordance with ISO 6860 and ASTM D522. The conical shape of the bending area allows the deformation of the test panel and examination of the elasticity range of a coating over any diameter between 3.1 and 38 mm in one single test. The sample panel is secured by means of two clamping knobs which has to be tightened and untightened by turning respectively clockwise or anti-clockwise.
SKU: SP1831 - Climate Testing, Coating Thickness Gages, Density, Dewpoint, Dry Film Thickness, Film Thickness, Gloss / Haze / Hiding Power, Gloss Meters, Hardness / Scratch Resistance, Hardness Tester, Material Thickness, PH / Conductivity, PosiTector 6000, PosiTector® 6000, Salt/Chloride Testing, Surface Profile, Temperature, Temperature and Climatic Testing, Thickness Testing
PosiTector 6000 Coating Thickness Gauge & Probes
Climate Testing, Coating Thickness Gages, Density, Dewpoint, Dry Film Thickness, Film Thickness, Gloss / Haze / Hiding Power, Gloss Meters, Hardness / Scratch Resistance, Hardness Tester, Material Thickness, PH / Conductivity, PosiTector 6000, PosiTector® 6000, Salt/Chloride Testing, Surface Profile, Temperature, Temperature and Climatic Testing, Thickness TestingPosiTector 6000 Coating Thickness Gauge & Probes
The PosiTector 6000 Coating Thickness Gauge is available in 2 models: the PosiTector 6000 Standard and Advanced. There are many probes to choose from either with a PosiTector 6000 gauge body or you may purchase a probe separately. See the PosiTector 6000 descriptions and downloadable pdf brochures in the description area below for more info.
SKU: n/a - Abrasion Testing, ASTM D2486, ASTM D3450, ASTM D4213, ASTM D4828, ASTM F1319, Hardness / Scratch Resistance, Hardness Tester, ISO 11998, Scrub Abrasion | Washability Tester Supplies & Accessories, Wet Abrasion Scrub | Washability Test
Scrub Abrasion and Washability Tester AB6000 & AB6010
Abrasion Testing, ASTM D2486, ASTM D3450, ASTM D4213, ASTM D4828, ASTM F1319, Hardness / Scratch Resistance, Hardness Tester, ISO 11998, Scrub Abrasion | Washability Tester Supplies & Accessories, Wet Abrasion Scrub | Washability TestScrub Abrasion and Washability Tester AB6000 & AB6010
The Scrub Abrasion and Washability Tester tests the resistance of paint, varnish or coatings to scratching, wearing, and color loss due to wet or dry abrasion.
SKU: n/a - ASTM D522, Elasticity Testing, ISO 6860, Resistance & Deformation
Bend Test Conical Mandrel Pro – SP1830
ASTM D522, Elasticity Testing, ISO 6860, Resistance & DeformationBend Test Conical Mandrel Pro – SP1830
The TQC Bend Test Conical Mandrel “Pro” is a laboratory apparatus to bend coated test panels over a conical shaped mandrel in order to assess the elasticity or resistance of a coating-, paint or varnish to cracking, elongation and/or detachment from a metal test panel in accordance with ISO 6860 and ASTM D522. The conical shape of the bending area allows the deformation of the test panel and examination of the elasticity range of a coating over any diameter between 3.1 and 38 mm in one single test. The sample panel is secured to the apparatus by means of a quick lever handle that lock and unlocks the panel in a split second using just hand.
SKU: SP1830